COMPOSITION
Two-component coating with epoxy resin as the base material and using a modified amine curing agent, this epoxy bonding paint features fast drying, strong adhesion, excellent water resistance and corrosion resistance, as well as good application properties of thick coating.
USES：
Suitable for equipment below the waterline and long-term soaking in seawater, this epoxy bonding paint can be used as an intermediate layer between epoxy primer and anti-fouling paint, enhancing the anti-rust effect and improving the bonding force between layers.
H53-200 EPOXY BONDING PAINT Tethnical Parameter
| ITEM | NORM | |
| Packaging specification | Paint: 18KG | Curing agent: 2KG |
| Appearance | Liquid | |
| Film color and appearance | Yellow, Matte | |
| Dry time,h,(25℃) | Surface dry h≤4 | |
| Hard dry h≤24 | ||
| Adhesive force,grade≤ | 1 | |
| Flexible,mm≤ | 1 | |
| Impact force,kg.c㎡ | 50 | |
| Salt fog resistance test,300h | No change | |
| Salt water resistance test (soak In 3% NaCl salt water for 96h) | No change | |
| Acid resistance (soak in 3% H₂SO₄ liquid for 48h) | No change | |
| Alkali resistance (soak in 5% NaOH liquid for 48h) | No change | |
Physical Parameters and Construct Specifications for Reference
| Life time after mix | 2h |
| Density after mix | About 1.5kg/L |
| Flashing point | ≤60° |
| Each film thickness | Dry film 40um,wet film 60um |
| Theoretical coverage | 0.2∽0.25kg/m |
| Advise coating layer | 1 Coats |
| Re-coat interval | 4h ,exceed 7days should be processed by polishing |
| Surface treatment | The surface of the base must be clean and dry , without loose paint, grease and other dirt , sandblasting or grinding to Sa2 grade. |
| Construction environment | Construction temperature is 5~40 ℃ Air relative humidity less than 85% . The substrate surface humidity is 3℃ higher than the dew point Avoid construction in the rain, snow, fog weather. |
| Coating method | Brush,Spray, Roller coating |
| Storage life | 1.5 Year |
Certificate
Guangdong Huaren products has passed ROHS certificate, ensure the products pass Europe standard ; has passed ISO9001:2015 certificate, ensure supply stable quality to our suppliers.
FAQ
Q: Are you factory or trade company? A: 100% factory,can offer you the best price. Q: What’s your MOQ? A: 300KG for easy production. Q: How long is the lead time? A: 5 days (Qty≤10 tons) , 8 days (Qty≥20 tons). Q: What’s your terms of payment? A: 100% T/T before production for LCL. B: T/T 30% as deposit,70% payment before delivery for FCL. Q: Can I use my brand? A: Yes, can use your logo and design.
Reason 1: The floor have too much water 2: No waterfloor layer. Prevention method: 1:First floor must be waterproof layer 2:Adopt moisture-proof system
Reason: 1: floor have too much oil Prevention method: 1: Knock down the old ground and remake it 2: If the oils is too much, please clear it firslty
Reason: Curing and the paint ratio is not correct Prevention method: The proportion must be accurate when mixing. It is recommended to pour the curing agent first and then the paint to stir.
COMPOSITION
Two-component coating with epoxy resin as the base material and using a modified amine curing agent, this epoxy bonding paint features fast drying, strong adhesion, excellent water resistance and corrosion resistance, as well as good application properties of thick coating.
USES：
Suitable for equipment below the waterline and long-term soaking in seawater, this epoxy bonding paint can be used as an intermediate layer between epoxy primer and anti-fouling paint, enhancing the anti-rust effect and improving the bonding force between layers.
H53-200 EPOXY BONDING PAINT Tethnical Parameter
| ITEM | NORM | |
| Packaging specification | Paint: 18KG | Curing agent: 2KG |
| Appearance | Liquid | |
| Film color and appearance | Yellow, Matte | |
| Dry time,h,(25℃) | Surface dry h≤4 | |
| Hard dry h≤24 | ||
| Adhesive force,grade≤ | 1 | |
| Flexible,mm≤ | 1 | |
| Impact force,kg.c㎡ | 50 | |
| Salt fog resistance test,300h | No change | |
| Salt water resistance test (soak In 3% NaCl salt water for 96h) | No change | |
| Acid resistance (soak in 3% H₂SO₄ liquid for 48h) | No change | |
| Alkali resistance (soak in 5% NaOH liquid for 48h) | No change | |
Physical Parameters and Construct Specifications for Reference
| Life time after mix | 2h |
| Density after mix | About 1.5kg/L |
| Flashing point | ≤60° |
| Each film thickness | Dry film 40um,wet film 60um |
| Theoretical coverage | 0.2∽0.25kg/m |
| Advise coating layer | 1 Coats |
| Re-coat interval | 4h ,exceed 7days should be processed by polishing |
| Surface treatment | The surface of the base must be clean and dry , without loose paint, grease and other dirt , sandblasting or grinding to Sa2 grade. |
| Construction environment | Construction temperature is 5~40 ℃ Air relative humidity less than 85% . The substrate surface humidity is 3℃ higher than the dew point Avoid construction in the rain, snow, fog weather. |
| Coating method | Brush,Spray, Roller coating |
| Storage life | 1.5 Year |
Certificate
Guangdong Huaren products has passed ROHS certificate, ensure the products pass Europe standard ; has passed ISO9001:2015 certificate, ensure supply stable quality to our suppliers.
FAQ
Q: Are you factory or trade company? A: 100% factory,can offer you the best price. Q: What’s your MOQ? A: 300KG for easy production. Q: How long is the lead time? A: 5 days (Qty≤10 tons) , 8 days (Qty≥20 tons). Q: What’s your terms of payment? A: 100% T/T before production for LCL. B: T/T 30% as deposit,70% payment before delivery for FCL. Q: Can I use my brand? A: Yes, can use your logo and design.
Reason 1: The floor have too much water 2: No waterfloor layer. Prevention method: 1:First floor must be waterproof layer 2:Adopt moisture-proof system
Reason: 1: floor have too much oil Prevention method: 1: Knock down the old ground and remake it 2: If the oils is too much, please clear it firslty
Reason: Curing and the paint ratio is not correct Prevention method: The proportion must be accurate when mixing. It is recommended to pour the curing agent first and then the paint to stir.