H53-30 epoxy mio barrior paint (10:1 ratio) is a two-component epoxy anti-corrosion coating with excellent adhesion, corrosion resistance and wear resistance. It is suitable for heavy-duty anti-corrosion fields, especially for long-term protection in harsh environments such as ships and steel structures.
Anti-rust pigments, additives, and organic solvents such as epoxy resins and mica iron oxide form the paint base, creating an epoxy mio barrier paint; polyurethane is used as the curing agent. When using, mix in a specified proportion, stir well, and use it within the specified time.
FEATURE：
This epoxy mio paint coating adhesion, good sealing ability, excellent resistance to permeability. With excellent antirust effect and the anticorrosion performance. Avoid exposure, to prevent the powder coating.
USES:
The epoxy mio coating is mainly used as an intermediate paint for matching epoxy or inorganic zinc-rich primer. It can also be used directly as an anti-rust primer for steel.
Salt water resistance test (soak In 3% NaCl salt water for 96h)
No change
Physical Parameters and Construct Specifications for Reference
Mixing ratio
Paint : curing agent=10:1
Life time after mix
2h
Density after mix
About 1.5kg/L
Flashing point
≤60°
Each film thickness
Dry film 40um,wet film 60um
Theoretical coverage
0.3kg/m
Advise coating layer
2 Coats
Re-coat interval
16h ,exceed 7days should be processed by polishing
Surface treatment
The steel should be sandblasted or polished to reveal the metallicluster, and have been coated with zinc rich zinc primer to removegrease, sundries and zinc salts.
Construction environment
Construction temperature is 5~40 ℃
Air relative humidity less than 85% .
The substrate surface humidity is 3℃ higher than the dew point
Avoid construction in the rain, snow, fog weather.
Coating method
Brush,Spray, Roller coating
Storage life
1.5 Year
Certificate
Guangdong Huaren Chemical industry Co., Ltd. products has passed ROHS certificate, ensure the products pass Europe standard ; has passed ISO9001:2015 certificate, ensure supply stable quality to our suppliers.
Service Advantages
Customization
Customized various performance coatings,according to the use situation,Design appropriate process and coating application plan.
Large-scale production capacity
The annual output of 30000 tons of coating and 20000 tons of resin has a large production baseof 20000 square meters.
Construction and technical services
Professional construction team, providing design, construction and technical guidance.
Timely delivery service
The subsidiary company of dangerous goods transportation company owned by the company can timely distribute large-scale key project projects.
H53-30 EPOXY MIO BARRIOR PAINT (10:1)
COMPOSITION
Anti-rust pigments, additives, and organic solvents such as epoxy resins and mica iron oxide form the paint base, creating an epoxy mio barrier paint; polyurethane is used as the curing agent. When using, mix in a specified proportion, stir well, and use it within the specified time.
FEATURE：
This epoxy mio paint coating adhesion, good sealing ability, excellent resistance to permeability. With excellent antirust effect and the anticorrosion performance. Avoid exposure, to prevent the powder coating.
USES:
The epoxy mio coating is mainly used as an intermediate paint for matching epoxy or inorganic zinc-rich primer. It can also be used directly as an anti-rust primer for steel.
Salt water resistance test (soak In 3% NaCl salt water for 96h)
No change
Physical Parameters and Construct Specifications for Reference
Mixing ratio
Paint : curing agent=10:1
Life time after mix
2h
Density after mix
About 1.5kg/L
Flashing point
≤60°
Each film thickness
Dry film 40um,wet film 60um
Theoretical coverage
0.3kg/m
Advise coating layer
2 Coats
Re-coat interval
16h ,exceed 7days should be processed by polishing
Surface treatment
The steel should be sandblasted or polished to reveal the metallicluster, and have been coated with zinc rich zinc primer to removegrease, sundries and zinc salts.
Construction environment
Construction temperature is 5~40 ℃
Air relative humidity less than 85% .
The substrate surface humidity is 3℃ higher than the dew point
Avoid construction in the rain, snow, fog weather.
Coating method
Brush,Spray, Roller coating
Storage life
1.5 Year
Certificate
Guangdong Huaren Chemical industry Co., Ltd. products has passed ROHS certificate, ensure the products pass Europe standard ; has passed ISO9001:2015 certificate, ensure supply stable quality to our suppliers.
Service Advantages
Customization
Customized various performance coatings,according to the use situation,Design appropriate process and coating application plan.
Large-scale production capacity
The annual output of 30000 tons of coating and 20000 tons of resin has a large production baseof 20000 square meters.
Construction and technical services
Professional construction team, providing design, construction and technical guidance.
Timely delivery service
The subsidiary company of dangerous goods transportation company owned by the company can timely distribute large-scale key project projects.